Q1) State the Aluminium Matrix Composites (AMC).

A1)

• This category contains the most Metal Matrix Composites. Aluminium Matrix Composites' matrices are often made of aluminium-silicon (Al-Si) alloys, particularly those in the 2xxx and 6xxx series. • Alumina (Al2O3) or silicon carbide (SiC) particles (particulate Composites) in amounts of 15-70 vol percent; • Continuous fibres of alumina, silicon carbide, or graphite in amounts of 15-70 vol percent; (long-fiber reinforced composites)

• Alumina fibres that are not continuous (short-fiber reinforced composites); The following fabrication procedures are used to make Aluminium Matrix Composites:

• Sintering (powder metallurgy);

• Casting with a stir;

• Surveillance. Aluminium Matrix Composites have the following characteristics:

• High tensile strength, even at high temperatures;

• High stiffness (elasticity modulus);

• The density is low;

• Excellent thermal conductivity;

• Excellent resistance against abrasion.

Automotive parts (pistons, pushrods, brake components), brake rotors for high-speed trains, bicycles, golf clubs, electronic substrates, and cors for high-voltage electrical cables are all made with Aluminium Matrix Composites (AMC).

Q2) Explain Magnesium Matrix Composite.

A2)

• Silicon carbide (SiC) particles are used to strengthen magnesium matrix composites (particulate composites) Magnesium Matrix Composites have the following characteristics:

• Low density; • High stiffness (elasticity modulus);

• Excellent wear resistance;

• Excellent tensile strength, even at high temperatures;

• Excellent creep resistance.

• Magnesium Matrix Composites are utilised in the production of racing vehicle components, lightweight automotive brake systems, and aircraft equipment such as gearboxes, transmissions, compressors, and engines.

Q3) Explain Titanium Matrix Composite.

A3)

• Continuous monofilament silicon carbide fibre (long-fiber reinforced composites); • Titanium boride (TiB2) and titanium carbide (TiC) particles are used to reinforce titanium matrix composites (particulate composites). Titanium Matrix Composites are made via powder metallurgy (sintering). Titanium Matrix Composites have the following characteristics:

• Extremely durable;

• High stiffness (elasticity modulus);

• Excellent creep resistance;

• Excellent thermal stability;

• Excellent wear resistance.

Titanium Matrix Composites are used to make structural elements for the F-16 jet's landing gear, turbine engine components (fan blades, actuator pistons, synchronisation rings, connecting links, shafts, and discs), automobile engine components, drive train elements, and general machine components.

Q4) Explain the Copper Matrix Composites.

A4)

• Continuous carbon (**C**), silicon carbon (SiC), tungsten (W), and stainless steel 304 (long-fiber reinforced composites) fibres are used to strengthen Copper Matrix Composites (particulate composites). Copper Matrix Composites are made using powder metallurgy (sintering) and an infiltration process. Copper Matrix Composites have the following characteristics:

• Low thermal expansion coefficient;

• High stiffness (elasticity modulus);

• Electrical conductivity is good

• Excellent thermal conductivity;

• Excellent wear resistance.

Hybrid modules, electronic relays, electrically conducting springs, and other electrical and electronic components are made with Copper Matrix Composites.

Q5) Explain Metal-Matrix Composites.

A5)

For the Space Shuttle, commercial airliners, electronic substrates, bicycles, automobiles, golf clubs, and a number of other uses, metal-matrix composites are either in use or in prototyping.

For the Space Shuttle, commercial airliners, electronic substrates, bicycles, automobiles, golf clubs, and a number of other uses, metal-matrix composites are either in use or in prototyping. While aluminium matrix composites account for the great majority of applications, a rising number of them require the matrix qualities of superalloys, titanium, copper, magnesium, or iron.

Aluminium-matrix composites, like other composites, are a group of materials that can be adjusted in terms of stiffness, strength, density, and thermal and electrical properties. To obtain the desired qualities, the matrix alloy, reinforcement material, reinforcement volume and form, reinforcement site, and fabrication method can all be changed. Regardless of the differences, aluminium composites have the advantage of being less expensive than most other MMCs. They also have good thermal conductivity, high shear strength, good abrasion resistance, high-temperature operation, nonflammability, low fuel and solvent attack, and the ability to be formed and processed on conventional equipment.

Casting, powder metallurgy, in situ reinforcement development, and foil-and-fiber pressing processes are used to make aluminium MMCs. With major producers ramping up production and lowering prices, consistently high-quality items are now available in big quantities. They're used in golf clubs, bicycles, machinery components, electronic substrates, extruded angles and channels, and a range of other structural and electronic applications, in addition to brake rotors, pistons, and other automotive components.

For components in jet turbine engines that run at temperatures above 1,830 degrees Fahrenheit, superalloy composites reinforced with tungsten alloy fibres are being developed.

Graphite/copper composites have tailorable features, are helpful in high-temperature environments, and have outstanding mechanical, electrical, and thermal conductivity. When compared to titanium, they are easier to work with and have a lower density than steel. Ductile superconductors were created using a copper matrix and niobium-titanium superconducting filaments. Heat sinks and electronic packaging are made of copper enhanced with tungsten or aluminium oxide particles.

The skin material for the National Aerospace Plane is titanium reinforced with silicon carbide fibres. The matrix materials reinforced with titanium carbide particles and fabricated into draw-rings and other high-temperature, corrosion-resistant components include stainless steels, tool steels, and Inconel.

Q6) Explain MMCs.

A6)

• Higher density-to-strength ratios

• Stiffness-to-density ratios that are higher • Fatigue resistance that is better

• Better characteristics at high temperatures

o — Increased power

o — Reduced creep rate

• Lower thermal expansion coefficients

• Improved wear resistance

MMCs have the following advantages over polymer matrix composites:

• Capability to withstand higher temperatures

• Resistance to fire

• Stiffness and strength in the transverse direction are improved

• There is no moisture absorption.

• Electrical and thermal conductivities that are higher

• Increased resilience to radiation

• There is no outgassing

• The ability to fabricate whisker and particulate-reinforced MMCs using standard metalworking equipment.

MMCs have a number of drawbacks when compared to monolithic metals and polymer matrix composites, including:

• Some material systems have a higher cost.

• Technology that is still in its infancy

• Fiber-reinforced systems require complex fabrication procedures (except for casting)

• No prior service experiences

Since the late 1950s, when work on MMC began, a variety of matrices and reinforcements have been attempted. However, MMC technology is still in its infancy, and more significant systems will probably arise.

Q7) Define the Solid-State Processing.

A7)

The main fabrication methods for solid state processing of metal matrix composites are powder blending and consolidation, and physical vapor deposition.

Metal alloy powder is blended with ceramic whisker/short fiber/particles in dry condition or in liquid suspension. After blending, the mixture is further processed by cold compaction, canning, degassing, and high temperature consolidation. There are some oxide particles in volume fraction of 0.05-0.5 depending on the powder and processing conditions that help Processing Methods Solid State Processing Power Blending and Consolidation Diffusion Bonding Physical Vapor Deposition Liquid State Processing Stir Casting Squeeze Casting Infiltration Spray Deposition In-Situ Processing dispersion-strengthening of the metal matrix composites. This method is usually used for the processing of aluminium and magnesium metal matrix composites.

The inter diffusion atoms at the metallic surfaces under pressure creates bonding between the metal matrix and fibers [14]. This fabrication method is widely used for aluminium or magnesium MMCs reinforced with continuous/discontinuous fibers.

Fibers are carried through an area with a high partial pressure of the metal to be deposited on a continuous basis. The vapour is created and introduced into the process, and then condensation occurs in this area, resulting in a fibre coating. Deposition occurs at a rate of 5-10 micrometres per minute. Hot pressing or hot isostatic pressing is used to consolidate the coated fibres.

Q8) Explain the Liquid State Processing.

A8)

a) Stir Casting:

Particulate reinforcements are combined with liquid metal melt, which solidifies the combination. A revolving impeller creates a vortex of molten alloy, and the pre-treated particles are injected into that vortex. The reinforcements are not consistently dispersed throughout the stir casting process, resulting in sediments in the molten alloy. In general, metal alloys can contain up to 30% particles with a diameter of 5 to 100 micrometres. Al-(10-15%) B4C MMCs are an example of this approach. Particles are inserted into the metal alloy in a semi-solid condition in another variation of the stir casting procedure.

Squeeze Casting

(b)An open die is filled with molten metal:

The dies are then closed, allowing the molten metal to solidify within the dies under pressure. Under high pressure and through contact between the metal and the die surface, heat is rapidly transmitted from the molten metal to the dies. As a result, this process produces a fine-grain casting with little or no porosity.

c)Process of Infiltration:

The porous shapes of fibers/whiskers reinforcements are infiltrated with liquid metal alloy. Depending on the level of porosity, the volume proportion of the reinforcements normally ranges from 10 to 70%. Binders such as silica and metal-based combinations are frequently used to maintain the integrity and shape of porous structures

d)Deposition of Spray:

Injecting particle/whisker/short fibre reinforcements into the spray results in a porosity deposition layer of 5-10% on the metal surface. The depositions are then further processed to achieve full density. Matrix metals are sprayed onto the fibres in continuous (long) fibre reinforced metal matrix composites. In this processing procedure, the fibre spacing and fibre layer have an impact on the fibre volume fraction and distribution.

Q9) What is Diffusion Bonding?

A9)

Diffusion bonding is one of the various vacuum processes to be aware of today (aka diffusion welding or thermo-compression bonding). Despite its specialist nature, this technology continues to gain appeal among design engineers and is finding increasing uses in manufacturing. Let's find out more.

A solid-state bond is a way of joining two or more mating pieces together that does not require the use of an interface layer (i.e., without the application of a material between the parts applied by plating, sputtering, ion implanting or brazing or in the form of a foil). The resulting interface must be bonded at or below the melting point of either the parent material or any formed eutectic (i.e., T bond T melting point).

A 50 percent or more increase in grain size is typical. To produce a high-quality hermetic seal, the total part strain must be in the range of 2-4 percent. Because of the strain requirement, a significant load (i.e., unit-normal force) must be supplied to the bonding surfaces to produce adequate results.

Q10) What is powder metallurgy, and how does it work?

A10)

Powder metallurgy is a metal-forming technique in which compacted metal powders are heated to just below their melting temperatures. Despite the fact that the process has been around for more than a century, it has only recently gained widespread acceptance as a superior method of making high-quality parts for a range of critical applications. This success can be attributed to the technique' benefits over other metal forming methods like forging and metal casting, such as material utilisation, shape complexity, and near-net-shape dimensional control, among others. Powder metallurgy is a renowned green technology because of these factors, which contribute to sustainability.

Figure 1 shows a complicated planetary carrier for a four-wheel drive torque transfer system, a helical gear and stainless-steel blades used in laparoscopic surgical scissors, an offshore oil platform manifold weighing over 6.5 tonnes, and a steel connecting rod used in V-8 engines. Powder metallurgy was used to create all of these parts.

Q11) Define Metal stirring.

A11)

Metal stirring in a coreless induction furnace had been a mystery until Inductotherm's research in the mid-1970s revealed the science behind the stirring forces. Until that moment, it was assumed that inductive stirring in an induction furnace was proportional to the furnace's meniscus height.

Meniscus height is proportional to kilowatts and inversely proportional to frequency squared. However, it became clear during actual melting operations that this simplified methodology did not provide an appropriate measure of stirring. Even though the meniscus heights were the same, furnaces holding the same amount of the same metal but running at different frequencies did not stir the same.

Q12) Explain the Rheo Casting Process.

A12)

Within the context of foundry technology, defects and anomalies are a daily challenge. The issue of quality becomes more critical as demand for castings with highly specialised applications grows.

The Rheo Casting process uses a semi-solid slurry, with the amount of advantages being directly proportional to the fraction solid at the moment of casting. A reduction in shrinkage and a large reduction in latent heat are possible benefits.

Defects, abnormalities, and faults in the final product are an unavoidable reality in the context of foundry technology. Because of the demand for better casting performance in order to create a high number of components with essential applications, this cohabitation between process and quality difficulties is becoming increasingly difficult.

During solidification, voids or cavities are created within a casting because to volume contraction, inefficient feeding systems, and/or gas (most commonly hydrogen) formation. Independent of the stress circumstances, interdimeric shrinkage pores, inclusions, and secondary dendrite arm spacing are favoured crack starting locations. These variables have a direct impact on the alloy's mechanical properties, resulting in lower strength and ductility, irregular fracture growth, and, in severe cases, material failure.

SSM-processing is a new manufacturing method for aerospace, military, and, in particular, automotive components. Suspension parts, engine brackets, and fuel rails for the automobile sector are made in Europe, whereas mechanical parts for snowmobiles and mountain bikes are made in the United States. With an emphasis on magnesium alloys, Asia has focused more on the production of electronic components such as electrical housing components and notebook chassis.

Rheocasting entails making an SSM slurry straight from the liquid alloy, then shaping it using a method like High Pressure Die Casting (HPDC). The alloy is cooled to a semi-solid condition and then put into a die without an intermediary solidification phase in "Rheo" procedures, resulting in a semi-solid slurry with non-dendritic solid particles from a fully liquid regular alloy. It is then cooled to the necessary fraction solid before being cast into a component. Component shaping directly from SSM slurries is intrinsically appealing because to features like overall production efficiency and energy management.

The ability to cast metal at a wide range of fraction solids is a key advantage of rheocasting. The majority of the process benefits of nondendritic, semi-solid alloys are proportional to the amount of solid present at the time of casting. Reduced shrinkage, less latent heat, and the degree of viscosity are all dependent on the percentage of solid in the alloy being increased.

Semi-solid casting, on the other hand, begins to vary from traditional die casting techniques as the solid proportion grows. Because of the much higher viscosity of the alloy, a more powerful shot end on the die cast machine is necessary for the larger percent solid material. In order to fit the wider hole in the cold chamber, the piston's stroke is normally longer. As a result, while high percentage solid casting reduces casting cycle time, it also necessitates more costly adjustments to the die casting process to accommodate the more viscous material. The schematic overview of the rheo casting method and microstructure of rheocast A356 alloy.

Q13) Explain Squeeze casting.

A13)  

The molten metal is put into the pre-heated die's bottom half. The upper part closes the die and adds pressure during the solidification process when the metal begins to harden. The amount of pressure utilised is substantially less than that required in forging, allowing for the production of intricate pieces. This procedure can be used to create holes and recesses using coring. Porosity is low, and mechanical characteristics are better.

This process can be used to make ferrous and non-ferrous materials.

Squeeze casting is a technique for shaping metal into shapes by squeezing two dies together. Unlike most casting procedures, which utilise two dies that are squeezed together before the metal is added, squeeze casting uses two dies that are pressed together after the metal has been introduced. The upper die is only removed after the liquid metal has cooled. The metal will normally come out stronger, with a nicer grain and less metallic shrinkage, if this process is used. Magnesium, aluminium, and their alloys are often utilised, although many other metals can be utilised as well.

In most casting procedures, two dies are used, but squeeze casting uses the dies in a unique method. Normally, the two casts are joined and liquid metal is poured into the casing. A pool of liquid metal is deposited in the bottom die, and a top die comes in and squeezes the metal into a shape using a squeeze cast. Because pressure is exerted via the upper die, this is not strictly casting, but rather a hybrid process that incorporates forging.

Q14) Explain the process of Squeeze casting.

A14)

Only liquid metal can be used in this application. While materials such as plastic can melt at high temperatures, this technique will not be suitable to cast plastic. After the upper die is set, workers wait until the metal is completely cool. Once cool, the upper die will be released and the required shape will have been cast into the now-solid metal.

Non-ferrous alloys like aluminium, magnesium, and copper alloy components are readily manufactured using this process. The squeeze casting process, combining the advantages of the casting and forging processes, has been widely used to produce quality castings. Because of the high pressure applied during solidification, porosities caused by both gas and shrinkage can be prevented or eliminated. The cooling rate of the casting can be increased by applying high pressure during solidification, since that contact between the casting and the die is improved by pressurization, which results in the foundation of fine-grained structures.

Q15) Explain Physical Vapor Deposition.

A15)

While all PVD systems use the same basic principles, some of the techniques for producing and applying coating material differ.

Thermal evaporation and sputtering are the two most prevalent PVD procedures. The resulting vapour phase is then condensed onto the target substrate in both cases.

Thermal evaporation, one of the most fundamental PVD processes, entails heating a material in a vacuum chamber until the atoms on its exterior have enough energy to be liberated, a process known as vaporisation. The atoms are vaporised and then sent via a vacuum chamber to coat a target substrate above the source material.

Sputtering is a plasma-assisted technique that uses high-speed plasma ions to create vapour from a source material. The atoms, clusters of atoms, or molecules of the evaporated source material travel in a straight line. A "substrate" such as a silicon wafer will be covered by a thin coating of source material if it gets in the path of these streaming particles.

The atoms of the source material atomically connect to the substrate to form a thin layer. Sputtering can be done in a variety of ways, including diode, ion beam, and magnetron sputtering.

A target item can be spun on several axes or placed on a conveyor belt that runs through the plasma stream to form a consistent thin coating of a few atoms or molecules thick. With the same deposition method, single or multiple coatings can be applied.

Reactive gases such as oxygen or acetylene can also be used in the deposition chamber to create an extraordinarily strong bond between the coating and the substrate. Despite the fact that the thin films created by these techniques are only a few microns thick, they are incredibly robust, making PVD an excellent choice for a variety of applications.

Q16) Explain Chemical Vapor Deposition.

A16)

Chemical vapour deposition is a versatile and widely used method that may be tailored to a wide range of applications.

The employment of one or more chemical precursors that break down the source material and transport it to the substrate, where it is deposited, is the main distinction between PVD and CVD.

The substrate material is placed in a vacuum chamber, and the source material is placed either inside the same chamber or in an adjacent chamber in the typical CVD sequence. After that, the source material is heated or the atmospheric pressure is reduced until it vaporises. The source material is then exposed to one or more precursors, which react with it and allow it to be deposited on the substrate.

The vaporised substance reacts with the substrate to form a thin layer that is homogeneous in thickness. The thickness of the film can be controlled by changing the temperature and time of the process.

In recent years, the development of high-temperature CVD procedures has opened the door to a plethora of new commercial applications. For example, researchers have begun fabricating graphene sheets and large arrays of carbon nanotubes using high-temperature techniques, both of which have enormous potential for the construction of new electronics and other products.

One of the key advantages of CVD is that it can produce uniformly thick coatings even on complex structures. CVD, for example, can be used to coat carbon nanotubes with a consistent coating in order to change their mechanical properties, such as making them chemically respond in a specific way.

Q17) Explain the Interface Reactions of TiAl/TiSi2.

A17)

As aforementioned, another excellent example for useful practice of diffusion pathway analysis is the Ti-Al-Si ternary system. The back scattered image of TiSi2/γ-TiAl annealed at 1,100 °C for 200 h is shown in Figure 10. Several phases including a porous layer developed at the interface of TiSi2 and TiAl. The phase sequence was obtained as TiAl/TiAl2/Ti2Al5/TiAl3 + Ti5Si4/Ti5Si4/TiSi/TiSi2. An irregular geometry of the Ti5Si4 phase was developed over a 100 μm layer thickness, in which the dark regions were observed as pores. It is noted that the Al solubility in the silicides (i.e., Ti5Si4 and TiSi) was detected to be less than 2 at %. However, the solubility of Si in the TiAl3 phase was detected to range up to 7 a t%, which is in agreement with previous results in which the large solubility of silicon in the TiAl3 phase has been reported.

The information about partial kinetics can be obtained qualitatively from the formation of the columnar Ti5Si4 phase developed in the TiAl3 phase. In order to evaluate the kinetics of the movement of components from the resultant morphology, the rate limiting component has been evaluated. When initial driving force for an interdiffusion reaction is a composition difference, the Ti and Al atoms would move towards the TiSi2 side, but Si would diffuse in the direction of the TiAl side. The columnar zone of the Ti5Si4 phase grows towards the TiAl side. If Si of the Ti5Si4 phase is the rate limiting component (D Ti(TiAl3) > D Si(Ti5Si4)), the feeding of Si atoms to the columnar Ti5Si4 phase determines the shape of the interface. Since the interface moves towards the TiAl side, the feeding rate to the point K’ is faster than that to the point K. Then, the perturbation would decay due to the faster movement of point, resulting that the planar interface develops. However, if Ti of the TiAl3 phase is the rate limiting component (D Ti(TiAl3) < D Si(Ti5Si4)), the arriving rate to the columnar Ti5Si4 phase establishes the shape of the interface. In this case, the arriving rate to the point K (the tip of the columnar Ti5Si4 phase) is faster than that to the point K’, resulting in the development of perturbations. Judging from the columnar morphology of the Ti5Si4 phase in Figure 10, the columnar Ti5Si4 phase grows through the TiAl3 phase, indicating that the rate limiting component is Titanium (D Ti(TiAl3)< D Si(Ti5Si4)).

The thickness () of the product phases was investigated as a function of the annealing time to determine the kinetic mode of each phase. The kinetics follow a parabolic law (2 = k t) when the intermediate phases increase through diffusion control. The thickness of the intermediate phases followed the parabolic law, according to the estimated data (Figure 12). The growth rate of Ti5Al4 was the most sensitive to the annealing period when compared to the growth rates of other phases. Despite the fact that the Ti5Si4 phase was developed as a porous structure, its growth rate is on par with that of the TiSi and TiAl3 phases, while the Ti2Al5 phase has the lowest growth rate of the product phases.

Q18) Explain the Metal matrix composites.

A18)

Metal matrix composites (MMCs) are made up of metal matrix mixed with other metals, ceramics, and organic substances. Reinforcements are typically used to improve the base metal's various qualities. The particle dispersion has a significant impact on MMC characteristics. As a basis metal in metal matrix composites, copper, magnesium, and aluminium have gotten the greatest attention [1]. These MMCs are widely employed in a variety of areas, including aeroplanes, aerospace, autos, defence, and others [2]. Silicon Carbide (SiC), TiO2, Aluminium Oxide (Al2 O3), B4 C, Y2 O3, Si3 N4, and AlN are the most often utilised reinforcements [3-7]. The Al2 O3 reinforcement has a high compressive strength and is resistant to wear. Boron Carbide is one of the hardest elements known. It has a high elastic modulus and fracture toughness. Boron Carbide (B4 C) boosts the hardness of MMCs but does not improve their wear resistance considerably [4]. Fibers play a significant role as reinforcement because they impart strength to the matrix, allowing the physical and mechanical qualities to be improved as needed. For improved wear resistance, zircon is commonly utilised in hybrid reinforcement [5]. A lot of work has been done on fly ash reinforced MMCs in the recent decade. Because they are inexpensive and readily available as a waste by-product in thermal power plants. It enhances the MMCs' electromagnetic shielding effect [6-8]. This research explores the effect of varied dispersion on the mechanical characteristics of MMCs, processing techniques, and their applications, based on the claimed potential benefits of MMCs. Many researchers have looked on MMCs that use a variety of metallic materials as a matrix. Al, Mg, Ti, Cu, and their alloys are the most attractive metals for industrial uses [8- 15]. Aluminium, both pure and alloyed, is the most studied material for use as a matrix in MMCs. Aluminium-based composites are excellent choices for structural use. As dispersion, several nano-sized oxides such as (Al2 O3, Y2 O3) [8-15], nitrides (Si3 N4, AlN) [12-14], carbides (TiC, SiC) [13-16], hydrates (TiH2) [7-9], and borides (TiB2) [8-13] were utilised. Ceramic reinforcing materials in these MMCs, carborundum, Sic, and alumina are commonly employed. Several researchers have also looked into other carbon allotropes such as carbon black, fullerenes, and carbon nanotubes [15-20]. CNTs are viable possibilities because they provide the metal matrix with extremely high mechanical characteristics. They also improve electrical conductivity, making MMCs a desirable material for electrical applications. MMCs utilise both single wall carbon nanotubes (SWCNT) and multi wall carbon nanotubes (MWCNT) as reinforcement. 0.1 wt. Percent copper MWCNT composites showed a 47 percent improvement in hardness and a bronze-0.1 percent increase in weight. Electrical conductivity was enhanced by 20% using SWCNT [18,19]. MMCs have also been found to disperse intermetallic complexes such as (NiAl, Al3 Ti) [15-19]. At high temperatures, Al– Al3Ti nanocomposite showed good mechanical properties, whereas TiAl–NiAl MMCs showed excellent hardness but poor fracture toughness and a poor socioeconomic standing (SES). In comparison to low SES children, high SES children have bigger median values for triceps skinfold, subscapular skinfold, arm circumference, and estimated mid-arm muscle and fat regions. High SES children have bigger values for all variables as compared to children in a US reference sample, while low SES children had smaller values. The disparities in arm fat area between the low SES children and the children in the other two groups, on the other hand, are bigger than the differences in arm muscle area. According to the findings, low-income Guatemalan children are more likely to suffer from chronic energy malnutrition than from protein malnutrition. For rural Guatemalan children, a similar pattern of energy deficiency has been seen. These findings show that estimates of arm fat reserves can be used to determine nutritional status in Third-World children. Muscle reserves are better than fat reserves as measures of nutritional status in underdeveloped nations, according to findings from rural Costa Rican and Honduran studies. However, those studies only looked at the extremes of the population distribution for muscle and fat and did not quantify cross-sectional muscle and fat areas.

Q19) What is Specific Heat?

A19)

For different aggregate types, the specific heat of concrete at room temperature varies between 840 J/kgK and 1800 J/kgK. Specific heat is sometimes expressed in terms of thermal capacity, which is equal to the product of specific heat and concrete density. The specific heat property of concrete is affected by a variety of physical and chemical processes that occur at high temperatures. This includes the vaporization of free water at about 100°C, the dissociation of Ca(OH)2 into CaO and H2O between 400–500°C, and the quartz transformation of some aggregates above 600°C [24]. As a result, specific heat is strongly reliant on moisture content, and it rises dramatically as the water-to-cement ratio rises.

KhaliQ and Kodur [27] collated data on concrete specific heat from a variety of research [16, 20, 24, 41, 44, 48]. Figure 2 shows how the specific heat of NSC varies with temperature, as reported in numerous studies based on test results and different standards. Up to 400°C, the specific heat of concrete type remains nearly constant, then increases to around 700°C, then remains constant between 700 and 800°C. The aggregate type has a major impact on the specific heat (thermal capacity) of concrete among the many components. The ASCE specified concrete specific heat relations [15] capture this effect. Carbonate aggregate concrete has higher specific heat (heat capacity) in 600–800°C temperature range and this is caused by an endothermic reaction, which results from decomposition of dolomite and absorbs a large amount of energy [12]. Carbonate aggregate concrete has a high heat capacity, which helps to reduce spalling and improve structural member fire resistance.

Q20) Explain Properties of aluminium reinforced with silicon carbide particles.

A20)

The ductility and strength of extruded SiC-p/aluminium-alloy composites were examined by Cocen and Onel. In this study, Al-5Si-0.2Mg was melt stirred with 9, 13, 17, 22, and 26 vol. Percent SiC-p (15-30m) and extruded at 500°C with a 10:1 extrusion ratio. The use of extrusion allows the clusters of SiC particles to vanish, the porosity of the composite to be reduced to extremely low levels, and the yield and tensile strength values to be enhanced by around 40%. The ductility of the as-cast composites decreases as the amount of SiC-p increases, however extrusion results in a significant improvement in ductility due to the reduction in porosity. They discovered that the yield strength and tensile strength of as-cast composites rise with the volume percent SiC-p up to 17%, then decrease with further reinforcement additions. The yield and tensile strength of an extruded composite rise in lockstep with the volume fraction of reinforcement. Sahin researched the preparation of SiC-p reinforced AMMCs as well as their mechanical properties. He used the squeeze casting technique to create composites reinforced with SiC-p (10 and 20 wt. Percent and sizes of 29m, 45m, and 110m). They looked at how density, porosity, and hardness were affected. Before removing the Al-MMCs from the mould, 3000kg of force was applied mechanically for 7 minutes to reduce porosity. After that, the mould was removed from the press and allowed to cool for around 20 minutes. He discovered that while density fell as particle size fell, porosity and hardness reduced significantly as particle size increased. When the weight percent of reinforcement in a composite increase, the hardness, porosity, and density of the composite rise. When compared to other particle sizes (45m and 29m) reinforced composites, the composite with a particle size of 110m achieves a homogeneous distribution of SiC particles; nevertheless, when the particle size is less than 110m, some agglomeration occurs. El-Galy et al. Produced and characterised functionally graded centrifugal cast Al-SiC-p MMCs. SiC-p with varying weight fractions (0, 2.5, 5, 7.5, 10, and 15%) and three different particle sizes of 16m, 23m, and 500m has been examined. For feeding the metal along the tube axis, three rotational rates of 800rpm, 900rpm, or 1000rpm were employed, as well as two controlled linear speeds of 16mm/s or 28mm/s. The concentrations and hardness of SiC particles in the outside zone of the cast tubes attain their greatest value, followed by a gradual reduction in concentrations and hardness in the direction of the inner diameter. The outer zone hardness increases proportionally as the weight fraction of SiC-p increases, although beyond 10 wt. Percent SiC-p, the rate of rise reduces significantly. Tensile strength increases as the weight fraction of SiC-p increases, while ductility diminishes. They discovered that ultimate tensile strength is proportional to the fraction of SiC-p in the particles and inversely proportional to particle size. The tensile strength increases linearly up to 10 wt. Percent SiCp, then decreases until it reaches 15 wt. Percent SiC-p. Venkataraman and Sundararajan investigated the tensile strength of SiC-p reinforced Al MMCs and discovered that when the volume percentage of SiC in the Al matrix increases, the tensile strength increases but the tensile density drops. Ozben et al. Investigated mechanical and machinability parameters such as density, hardness, and impact resistance. 10 ISSN: 2456-7108 ISSN: 2456-7108 ISSN: 2456-7108 Patel et al., Adv. J. Grad. Res., Vol. 5, Issue 1, pp: 8-15, January 2019; available online at Journals.aijr.in Patel et al., Adv. J. Grad. Res., Vol. 5, Issue 1, pp: 8-15, January 2019 AlSi7Mg2 reinforced with 5, 10, and 15% wt.% SiC-p (30-60 m) was tested for toughness, tensile strength, and machinability. To improve the wettability of reinforcements, 2% Mg is added to Al7Si alloy. The ratio of 50–60 m particles remained lower than the ratio of 30-45 m particles in the particle size range (30-60 m). The use of varied sized particles is justified since small particles in a higher ratio aid in increasing strength while larger particles aid in achieving a homogeneous mixture. Hardness and density of MMCs rose with higher reinforcement ratio, while impact toughness dropped, according to their research. They also discovered that tensile strength rose up to 10% SiC-p reinforced and dropped when 15 wt.% SiC-p reinforcement was utilised. Surface roughness and cutting tool wear increase as the feed rate or particle ratio is raised. When the cutting speed of AlSi7Mg2-MMC samples was reduced, the surface quality increased. Rao et al. Conducted an experimental study on the mechanical properties of Al7075/SiC-p composites and discovered that increasing SiC particle size and weight percent significantly increased the tensile strength and hardness of the composites, but lowered the ductility. Ozden et al. [13] studied the impact behaviour of aluminium alloy (2124, 5083, and 6063 Al alloy) reinforced MMCs with hot extrusion ratios of 13.63:1 and 19.63:1 at different temperatures, i.e., -176 C, 21 C, 100 C, 200 C, and 300 C. They discovered that using SiCp as reinforcement in an Al alloy ductile matrix reduced the matrix's impact toughness. Increased particle size and hot extrusion ratio enhanced the impact toughness of the composites slightly, while artificial ageing reduced the impact toughness of all unreinforced alloys and composites. The impact behaviour of unreinforced AA5083 and AA5083-SiC-p composites was unaffected by the test temperature. The impact strength of composites based on AA2124 and AA6063 alloys decreases at 100 degrees Celsius. Meena et al. Investigated the mechanical properties of the created Al/SiC MMCs using a stir casting technique in which AA6063 was reinforced with SiC particulates (weight fractions of 5, 10, 15, and 20%) with mesh sizes of 220, 300, and 400, respectively. Proportionality limit, tensile strength upper yield point, tensile strength lower yield point, ultimate tensile strength, breaking strength, hardness, and density all increased as reinforced particulate size (220 mesh, 300 mesh, 400 mesh) and weight fraction (5 percent, 10%, 15%, and 20%) of SiC particles increased, but percent elongation and percent retraction decreased. Impact strength diminishes as the reinforced particulate size is larger, but increases as the weight percentage of SiC particles grows.